Its that time again boys, knife fags stay out.Today's question, Does anyone here dislike the smell of metal?
>>2219237nickel is the only metal that smells and tastes good imo
>>2219237I HATE the smell and taste of metal. Copper is the worst of them all.
I got some high quality investment casting and want to do small silver castings through lost wax method. Do I have to use a pressure chamber to not get bubbles or can I vibrate it well enough?
>>2219237>>2219255The reason metal has such a distinctive and sometimes overpowering smell is because it's the same scent as blood.
>>2219237what is that fuzz? zinc whiskers?
>>2219274If the mold is HOT and the metal is high fluidity some rotation/vibration is good enough. If it is a viscous metal you really want either excessive sprue pressure+lots of side-feed tubes and vents if you cant use vacuum.
>>2219562Yup. Pretty weird!
>>2219237Ah yes the RoHS whisker
Anybody here work in a materials testing laboratory? Sounds like a nice job.
>>2219237Ever since I read the Gingery books, I've wanted to make a lathe from scratch. A small cast aluminum lathe bed with a screwed on piece of CRS seems like a shitty idea though, so I've been thinking about trying cast iron. Is casting a lathe bed in iron even attainable in the home foundry? The crucible would have to be pretty huge.
>>2221796i work closely with one, they're probably sick of being drip-fed funding to work on retarded problems.>stop forging a part to save money>WTF why does this part break?>send it to the lab, top priority, red alert>oh wow the microstructure was worse, who could have guessed?
>>2221855If you stopped forging it, what was the fabrication process that replaced the forging process?
>>2221855That sounds like 95% of my WOs. "This part breaks!" "Oh yeah, the plant substituted the 4140 with 1020 because it was cheaper..." Or my favorite: they substituted high-grade stainless with free-machining leaded steel and didn't know why it was dissolving in the food tanks at the customer's customers. I actually forwarded my report to legal. Fuckin' hell.
If I inhale zinc fumes can I quickly use something to block it? Like if I eat 10 radishes?
>>2221828a year ago i stumbled over a boomer blog where he is attempting just that, casting his own lathe.afaik he is using an oil burner and scrap cast iron stoves for the carbon content. dont remember the site name thou
>>2222875No, stop doing that or wear proper PPE.
>>2223034My uncle from China (no blood relation) says they used milk. Apparently the lactose intolerance diarrhea purged the lead and zinc from their day at the recycling smelter.
Could I use Ar gas over a DC stick welder to get a little extra quality or does the stick flux require oxygen to melt and stuff?
>>2221828CRS?>>2224044I've heard northern Europeans recommend drinking milk. They are not lactose intolerant.
>>2219633I think he's talking about the initial forming of the mold, rather than the actual casting
>>2221828I've wondered the same thing, or failing that what about bronze? Would that be suitable? It would be better than aluminum at least, I assume.
>>2219562 Used conduit strap covered in insulation
>>2219237Fun FactJews can smell gold.
>>2225219You probably could, although pouring that much bronze has it's own issues. But I don't know if you could keep the ways flat and accurate, as bronze - while tough - wears faster than steel, which is why bronze is used for bushings. Never heard of or seen a metal lathe made out of anything but steel, with an iron base. But it's pretty dense, so it may have enough dampening properties for a lathe. The issue with aluminum is strength, and it's too light. You don't want the machine flexed and shuddering all over the place. I haven't checked metal prices in a while, but bronze has always been pretty pricey, too - the cost factor of bronze is something to consider. Don't know for sure if it would work -my gut feeling is it's too soft to keep the ways flat and accurate, but who knows? I kind of feel if it was appropriate, you'd see bronze milling machines and lathes, and you just don't. Like a Bridgeport - the base is just cast iron, but the important bits that you need for accuracy are steel.
>>2221828Iron is too soft for the accuracy you'd need for the ways. Maybe an aluminum frame, with steel inserts. But then you'd probably have vibration issues.
>>2225190>CRS?Cold-rolled steel>>2221828What about concrete? I heard the density is comparable to aluminum.
>>2225314Concrete, in MY aluminum? It's more likely than you think!
>>2221828Those books are for bored owners of existing machine shops and not a way to get machine tools. If you want to make a useful result begin by setting up an effective shop and don't waste effort and metal on anything BUT the shop and its equipment. Tools get you toys but rarely the opposite. Begin with welding equipment (which helps build many other things like racking, benches, machinery dollies and much more). Acquire machine tools, tooling and learn how to obtain stock. Everything that bleeds time and money from your shop works against you.
Any handle advice? Its a kitchen knife
>>2227999I would honestly just wrap some thick string or duct tape around the handle.
>>2228020Ive done that, Doin mahogony, I think.
>>2228091You know there's an actual knife thread?Are those made from old files or something like that?
>>2228093I did not. Searched "forge" and found this one. But anyway this one was a leafspring
>>2228093Knife autists are weirdos and lack ANY metallurgical sense, artistic inspiration, or class. They pay $1000 for some snowflake powdermet knife that is as good as 1040.This is the much better thread!
>>2228311It's a knife making thread, not a knife consoomers thread.
>>2219237What would be some viable routes to source some ingot molds of particular/custom dimensions? If I were to make my own molds would I necessarily be limited to using cast iron or would other materials like stainless steel be acceptable?>>2226757thank you, these insights will save me time and money>>2221874>leaded steel ... was dissolving in the food tanksoof
>>2219237Not rly. But i snort a line of borax every morning,
>>2229360I do a line of asbestos furnace liner.
Whats stopping me from using E6010 to make a temporary weld on austenitic stainless? Should I use a bladed or abrasive saw to cut?
>>2230295Pffff. Your furnace is literally a bong, and you're sniffing the bongwater, thinking you're cool.
>>2230889Also, what thickness of stainless sheet is considered structural for light applications (for example a chair)?>Should I use a bladed or abrasive saw to cut?Shears are also a possibility since I'm working with sheet metal.
>>2230899>what thickness of stainless sheet is considered structural for light applicationsI'm looking at using 330 (building a furnace with the potential to upgrade it to a gas turbine) and 303, 304, or 430 if that helps.
>>2230914You can weld it if you want but the weld will rust quickly.Any thickness is structural if you dimensionally strengthen it. I recommend 1/12" at least if you have a nice bending shear. Use an abrasive cutting wheel unless your bladed cutter is carbide tipped.
Can anyone give me a rundown on the actual process of metal recycling? I ended up thinking it a few weeks ago at work. We machine low alloy steel, stainless, bronze, CuNi, monel, inconel, titanium, and aluminum, and all the chips end up going into a single container. The magnetic steels can of course be pulled out with a magnet, but I don't know how everything else is dealt with. Can the metals be melted fractionally?
>>2231057>dimensionally strengthen itCould you elaborate?
>>2231193Like automotive drawn steel. You add dents and bends which make floppy sheetmetal stiff.
>>2231068A search engine would provide vidyas of different processes.
Hi /metallurgy/, /lit/ here. I got a brass pen, will letting it tarnish actually damage the pen or is it purely aesthetic? (I know that rust can really fuck up iron, so I'm wondering)
>>2231317Brass, bronze and copper don't really rust, they just get patina and stop oxidizing (unless obviously exposed to some caustic stuff).
>>2231227Is that a steam engine or internal combustion?
About... Halfway done? Probably gonna do a hilt for it.
>>2233591What's the end application? Wood splitting? Head splitting?
>>2233657A bit of both, actually. Gonna do a converce grind
>>2233591Don't forget to carve out a cow's foot for authentic look.
Im trying to compress and hammer harden a bronze dagger.Ive seen some diy set ups to do a unified and consistent edge by using two brass door handles as guides with the blade run through it as its hammered.Problem is all my door handles turned out to be fake brass or hallow.Ive got some round brass but im not sure what set up i could do quickly to keep them in place as guides.Pic is an example in use with door handles.
>>2233773Peen the edge out (Like they did in the bronze age you modernist coward!) then grind into the peening to make a straight edge. Or just weld two hardened steel strips to a standard steel hinge in such a way that it draws out the edge.
>>2234101>Peen the edge out (Like they did in the bronze age you modernist coward!)They didn't.thats the funny thing.In European bronze age swords the hammer hardened edge is so neat and uniform that bronze reproduction Smiths agree they have been using a tool for a guide.
How flat should flat stock be?I bought some annealed 1095 blanks on ebay to make some bladesThey arent very flat, and one is pretty bowed.Is this to be expected or not?I bought some 01 tool steel a long time ago for a blade I never finished, and it showed up perfectly flat
>>2234622Flatness costs extra.Seriously, it is extra. Check on McMaster.
silver that turned black smells disgusting
>>2222884Ohshit, if it's the blog I'm thinking of I used to read that maybe 10 years ago. did he ever finish the lathe?>>2221828>The crucible would have to be pretty huge.Maybe not too bad, you could rib a "flat" pattern out to get your rigidity without needing too much additional volume. The few times I've pulled by Enco mill/drills bed off to clean the ways, I've been """"impressed"""" by how little iron is actually used to make it. Same would probably apply for aluminum, too, though. you could always face an aluminum casting with a grey cast sheet that you can lap down.
I'm working on unbending flattened aluminum pipe. Since I can't get a visual when the Al reaches forging temperature. I'm just going to start heating it with a torch, shove a glowing hot steel wedge (pre-forged to the rough dimensions of the bend), then fine tune the wedge using the pipe's bend as a forging die. I am hoping when the wedge assumes a fine shape, heat transfer from the steel to Al will be maximal, as I continue to hammer, eventually the steel will recrystalize and harden, while the Al will be in a hot-working state. The pipe will then be soft enough for the wedge to hammered through the bend, effectively straightening it. I will follow with a water quench. Though IIRC, there are limits redoing the heat-treatment on precipitation-hardened Al. What could be done differently to improve the success rate?
>>2225256interesting.. so they're of dwarven blood after all
>>2235203What would a modern-day elf smith be? Some guy running a $5Mil CNC from programs he found online to make decorative birds out of copper?
>>2236125>cncSounds like the work of Sauron. An orcish smith, perhaps, but an elf no longer.
metal has no smellthat shit you're smelling is your own skin oilshttps://www.youtube.com/watch?v=BqLH-nTZEOc
>>2236655Does machining oil not break down the same way?
>>2238041depends on how volatile it is
What is this golden metal used in high-frequency RF stuff? Looks fancy.
>>2239422Probably oxygen free copper
How can I find tin in the wild? I came across a bundle of zinc wheel weights a few months ago and made some brass, now I want to try making bronze with tin.The only thing I can think of is pewter, but even thrift stores that have it seem to know its worth something.
>>2239563lead free solder
I need to make a tiny leaf spring to repair an antique. I bought some annealed 1095 sheet to make it out of, but do I need to quench it in water or oil when I harden it? since it's so small should I put it on a plate and heat it indirectly?
>>22397731095 is slightly tricky because optimal ht requires a hold time at aus temp.You might be able to get away with no hold, but it won't be optimal. 140 degree canola or fast quench oil.After quench clean scale to shiny metal then use torch to gently heat until steel turns light blue. Dunk in water and repeat once or twice more.
>>2239836I was going to niter blue it to temper it. I did it before but it was a bigger spring.
>>2239890Antiques leave a LOT of room for error. Not exactly a performance car.
>>2239422It's probably Gold. you can't use a conformal coating on HF guides and cavities without fucking up the characteristics, so they generally do gold or gold-on-nickel. You never leave bare copper in an open RF cavity if you expect it to last.
>>2239422Sometimes I think its coated aluminum
>>2241524it is. if it's a gold plating the gold will only be a few microns thick.
With all this welding, machining, casting and what not...are there any health risks I should be aware of? Metallurgy is interesting to me but I always think back to this former welder in his 50s had neurological issues that he blamed on his occupation. I don't want my brain or lungs to be fried.
>>2241726Don't breath zinc fumes or welding fumes. Wear proper ppe when grinding. The abrasives are similar to asbestos in your lungs and you're also inhaling metals.
>>2241772Can I ever get shit out of my lungs?
>>2242932Depends, but the answer for a lot of bad shit is no.
>>2219242Nickel tastes like cocks, so i'm told.
>>2243493I can say with certainty nickel plating does not taste like my penis.
>>2244465based Marylyn Manson aficionado
Can I do easy nickel plating at home or are all the good chemicals banned now?
>>2245665It's hard to get the really good shit anymore but if you have a DC power supply and some scrap copper and nickel you can get some good solution going with distilled drain cleaner.
>>2239422It's literally gold. Same as you would do with a normal FR4 PCB with ENIG/ENEPIG finish.
>>2246078Can I make money stealing the microwave antennas from cell towers and finding gold?
>>2242932No but you can start wearing masks when you work with that shit from now on. All the old guys will make fun of you and say pants on head retarded shit like "you gotta die from something lol". Fuck them.
>>2219255>>2219548metals have no inherent smell seeing as they don't vaporize under normal temperature and pressure (except mercury I think), the interaction of chemicals and oils (like on your hands) is what gives them smell.
>>2221828if you can cast iron you can cast in sections and bolt them together. also concrete the like other guy said or granite epoxy is an option>>2225266you're dumb. lathes and Mills from the $800 hobbiest benchtop to the $8000 professional tool room are made of cast iron for the weight and vibration dampening. it's only when you start getting into fuckhuge industrial machines worth four times your house that they're made of steel since they're so heavy and under so much stress they would crack cast iron and they weigh so damn much anyway rigidity isn't an issue
Plenty of resources online for casting aluminum bronze but I want to make ingots that I can smith later. Is this doable?
>>2247369sure why not? just cast it into whatever ingot mold or (seamless) pipe of the size youre looking for. or if you already have casting sand then make sand molds of your desired ingot
>>2247369Ive done it You can buy a cheap iron ingot mold.Ive found the porperties of aluminum and copper behave differently to tin and copper bronze though.Its normally a straightforward alloy (tin bronze) but for some reason despite aluminum having a lower melting point to copper it doesnt seem to mix with it easly and remains pretty viscus at the bottom of the crucible while the copper is pretty much water above it.It took a great deal of mixing , borax and letting it sit before they made a useable alloy.
>>2247461That was the copper-rich weird shit. To the right of "L". You need to get above the melting point of copper to reeaalllyyy get a 100% melting.
How much would it cost me to build a working prototype of this engine?https://grabcad.com/library/wankel-rotary-engine-5
>>2247452>>2247461i know it can be cast, i want to forge it hot with a hammer afterwards, like I would steel.
>>2247637i also found it rather indifferent to tin bronze.A lot of people made a big deal of it being one of the strongest bronze alloys and difficult to machine.But i found it really easy to belt sand and polish.Certainly didint behave like a tough materiel perhaps the aluminuim content was lower than 12% cant have been higher as there was still some Aluminium left at the bottom of the crucible.As i heard higher than 12% it gets brittle.
>>2247148Go ahead and see if you don't get cooked first
Is steel casting even viable without having an induction heater?
>>2247872Oil heat or an excess of propane will do you just fine. Try to use the steels with an extra pinch of Silicon for flowability.
>>2247933I'm more worried about the casting furnace starting to degrade at steel temps, with induction I just have to worry about buying new crucibles every few pours
>>2247949Oh, yeah... You are right about furnaces degrading faster. But some mineral fiber reinforced clay and don't be afraid to slap that shit on.
tried asking in /k/ but then I remembered that none of them own guns.I'm doing a mac11 build and I wanted to nickel plate it and polish it to a mirror sheen for maximum swag. will there potentially be any problems if I also end up nickel plating the inside of the barrel and chamber and the bolt as far as head spacing and other critical dimensions? obviously plating deposits metal, but would it be enough to cause any serious problems with a simple blowback gun like the Mac?
>>2248114Depends. Aesthetic flash Nickel over flash copper for a wall queen that you might need to shoot one day? Nah. Hard nickel that will actually resist wear? Absolutely will fuck it up if you don't cover the actions and barrel insides.
>>2248116that's about what I figured. I'm not totally sure how thick of a coat I can generate but it was just going to be simple YouTube tutorial electroplating crap, so nothing crazy but still I'll plug up the barrel and probably skip out on the bolt, it comes blued so I'll probably just leave it that way.
>>2248114once you've nickel plated it you'd might as well gold plate the nickel
What are the best brass recipes for aesthetics?
>>2248244High-copper for that classic sheen or add a lot of Nickel to get white-brass. Avoid zinc, zinc is for fags.
>>2248244Use gold instead.
Any jewelry fags? I've been getting into making jewelry from scratch. So far only sticking to silver cause its cheap but I plan on eventually making gold jewelry for myself and to sell. Currently making a Cuban link ring pic related, it takes a long time but it feels nice "actually making something" with your hands since I'm a neet.
>>2250461A NEET jeweler? How does this work?
>>2250638That link ring is for Homura-chan
>>2250671What are you, the 4Chan tester?
>friend has a crossthreaded to death aluminum thing he wants permanently welded>only have DC tig/stick welder with no tig gear yet on hand>didn't find aluminum rods at cambodian tire>bought some brazing rods and a torch but never brazed beforeI was kind of in a hurry so I didn't even stop to consider if it was a good idea or not. Would it work or should I just go to a welding supply store and get actual welding rods?
>>2250997Brazing Aluminum...? In open atmosphere? Without experience? On an unknown alloy? Just flame-tip weld since you have a torch already. If you are careful you don't need any filler rod. Or is this thing so blasted you need filler metal?
>>2251020well it's basically pic relatedMy first inclination would've been to just fill it with a nice weld all the way around but if I do it using a propane torch I don't really know what would be the correct course of action to make it solid and not look too much like shit
>>2250638More like a jewelry hobbyist. I don't have a job I'm just learning to make stuff from youtube. Got a lot of needed tools >>2250670Its for my pinky
>>2251277 Pinky chain ring...?
>>2250997You can weld aluminium with acetylene torch, pajeets repair stuff that way. Even engine cases.
Cross posting from biz as I think I'll get better responses here.I have the opportunity to get a job pouring gold for a small mining & processing site.I want to know if gold pouring/precious metals casting is an actual profession/line of work or am I imagining it? I'm told its skilled work so I want to know if this is a skill that would get me work in the future, especially if I get good at it. I imagine for firms producing bullion the process is mostly automatic but could this experience get me somewhere like that?Searching for "gold pouring jobs" just returns a bunch of news pieces so I'm a bit lost.
>>2221874>leaded steel... was dissolving the food tanks
>>2252603Technical and skilled labor? Yes. Builds a record of trust in jobs that require high security? Yes.Will it ever get you a job outside of pouring ingots for precious metal refiners...? No. You will be stuck in that profession for life unless you get a security license to do security work for transfers or get a trade license to handle warehouse receiving/fulfillment for precious metal storage.
>>2252603One of my first experiences if the net as a kid was joining melting casting user groups. Picrel gave me Lels.You know a cupola is the traditional way of casting metal at home right?>Fuck propane cucks
how feasible is diy aluminum extrusion?this is basically the only vid i can find on the net of someone doing it non commerciallyhttps://www.youtube.com/watch?v=obWFprWTRSs
>>2252763Thanks, this is the sort of reply I was hoping for. I can't say I expected other jobs to just fall into my lap based on this work alone so jumping through those other hoops seems rational.Can you comment at all on salaries at these refineries?>>2252782>deliberately causing more pollution than is necessary>sheer heft intimidates lesser gas furnacescuploa kings keep winning
So i got a question about making a tap and die regarding how to make them from scratch without machinery cause i remember looking at the colonial gunsmith video on youtube and seeing recreated old looking tap and dies and wondered how did one make it from scratch back then and wanted to ask you guys if you had any answers on how to make them by hand.
>>2253427Ye olde die tool
>>2219237Defuk did you do the get your metal bracket to grow a mold like that? I understand that it's not a mold, but im curious to learn more about thllpic related
>>2253431It's actually a huge disagreement in the metallurgy community. There is no consensus.
>>2253427Single point thread cutting. Hand-filed die to make a screw. Cut the screw into a tap and harden. Screw into a metal piece and file cutting edges to make a die.
I've got a chance to buy a 150lb anvil for $300 bucks. Looks too good to be true though, especially with what looks like a hackjob attempt at welding at the waist. What do you guys think?
>>2256074"Better Than Nothing™"
>>2219237I work at a steel foundry and can't smell it at all anymore unless we use a metal that gets made once every few months. Smells like pineapple.
>bought welder>dream about welding stainless and shit, what kind of cool things i can make out of it>check prices>shit is more expensive than fucking copper pipeDamn. Why is stainless so expensive? I always thought it is cheaper than copper and aluminium, but apparently shit goes like this: black steel < aluminum < copper < stainlessAlso, which material is most based?
>>2256299It IS cheap if bought direct in bulk. Small-load dealers use a 400% markup.
>>2252565Yeah its a commercial style
>>2256455Should have made it Gold, poorfag.
does anyone know what to what hardness/temperature i should temper a screwdriver? want to make a special size Flathead that doesn't shatter and pierce my eyeball
>>2257582HRC60. Any tool steel with a lot of Chrome, Vanadium, and Molybdenum. Oil quench, anneal, oil quench.Temper at like 400F for 5 minutes or so. Grind to final shape.
>>2257619QUALITY NORTH AMERICAN CAST IRON!
>>2258883i will use a DIN alloy just to spite you
Hello its the bronze sword guy again.Im wondering if i can get some advice and info on brazing. Ive been experimenting with some miscasts to see if i can fill some superficial holes.I havent had much luck with a propane trouch and some flux nothing seems to stick.I have heard in the bronze age they would "wash" miscasts with holes with a coating of fresh bonze on top so i attemped that but didnt have much luck with the bronze droplets not actually sticking or fusing securly.Whats the chemistry behind liquid metal fusing? i clean the surface, add flux and heat it up.Some chinese blades are made from multiple parts cast onto each other.How does that work if the metal doesnt fuse?
>>2259041Too cold. The molten metal should be over-heated and the base metal should be pretty damn hot.Your drops are chilling before they metallurgically fuse. Another trick is to fill it with a more chemically active lower melting point metal like a lead or tin.
316 IS FOR FAGSTHIS POST BROUGHT TO YOU BY 304 GANGSTAY STAINLESS, MY FRIENDS
>>2259132Ah i see so should try propane tourching the blade till red hot while pouring on fresh bronze from the crucible? But what about the chinese blades they were fused using clay casting how would they have heated the center spine within the clay mold before pouring the edges into mold?
>>2259227Heat the molten metal HELLA HOT and pre-heat the mating mold+part under air-forced coals.
>>2219237What kind of startup costs are we talking if I want to use my 3d printer and cast my prints?
>>2259858that depends on the kind of random stuff you have laying around. you need oilsand. if you buy this is by far the biggest expense, but i guess mixing your own is a huge pain and requires a lot of sieves. the castbox is simply done with 2x4s+ like 20$ for random stuff, brush, blower, parting powder etc. the foundry can be rigged up out of dirt and random bricks/stones. a natural draft airflow and spalted wood should get you to aluminum temperature range easy. i say sub 100$ without safety gear.If you want to go up to copper/bronze, forced air and an insulated foundry is a must. For forced air, a mains leaf blower and triac speed controller is like 50$ on ebay. you'd also need coal for fuel and a refractory lid
>>2259864Bounce house fans are cheap too and sling a lot of air. They're continuous duty. I have three for welding ventilation and want more.
>>2228089Not samefagging, but that knife looks awesome
So a friend of mine wants an African style machete like pic related. I am not sure what steels to use. I was thinking, maybe a "leafier" core and a harder edge. It must be able to be used for machete related tasks like chopping wood and stuff.Ideas?
>>2260229Unironically buy a large commercial-grade lawnmower blade. If you need a harder edge you can do some cheeky heat treatment with a torch.
>>2219237Bruh why did you stick pubes to that
>>2260229Why do he want to be machete warrior
>>2260229leafspring and a 45° bevel
>>2260282Sounds good.>>2260351He lives innawoods and uses the machete to chop wood and form wood for different stuff. He's been in SA and well, the machete is his preferred tool now.>>2260388Also an idea.
wood chip anon from last year here,Im in the process of building a new furnace/forge combination, it will be coal fired and able to operate horizontal and vertical.Im building this out of an old compressor jug, can probably stuff 3-5cm internal insulation (outside could be wrapped too)>>https://www.instructables.com/Beer-Keg-Metal-Melting-Furnace/that dude did a mix of sodium silicate, perlite and corundum to fire his own ceramic insulationis this a legit way, or am i better off with ceramic wool and a thin refractory mantle? I plan to go well over 1200°C, ceramic wool is only rated for that
>>2260557if i choose to do a inner ceramic wool liner, will i get cancer if i leave it uncoated? will be only operated outdoors
>>2260594Probably yes. Coat it.
>>2260594Yes! do not do this.
Awwh yeah bois alright here I am thank you for coming home ok so thank you thank you yes so I have recently acquired 30 acres in colorado and I am contemplating blasting the shiznatt out of it and mining it and yes actually thank you I have like almost no experience doing anything at all whatsoever soSo uh ok I think we're going to assume for practical purposes that these are uh marxian mines and by that I mean they contain an equal distribution of all the ores to some extent relative to their r err relative prevalence as a natural resourceExcept of course if you have any knowledge concerning geographical geology. Then any advice there would be appreciatedSo like from this theoretical perspective it's fun to assume we're looking at shale. If were looking at lime then I'm thinking concrete but silicates good for cement tooSo I'm going to attempt my best question here: how feasible is it to separate each of these elements [crude elements or otherwise to any extent] from another to transform raw earth into useable resourceUnlimited concrete can be transformed into like a plaza of unlimited swimming pools. Metals would be awesome too.Then advice concerning furnace structure could be important too And stuff. ThanksAlso this thread gets nuked sometimes. Why. This is ultimate diyAlso I'll be going back to basics soon doing DIY experimental stuff with kilns and stuff so if you could lend me some advice with furnace theory I'd appreciate
>>2260791Ultimately I want a pyramid. Like a fortress castle pyramid thing. The weight of it I have estimated at $250000 in concrete. This borders justification of unlimited concrete. I hate to tell you this because you're terribly clever people and you might have meaningful manners whenever you disagree without me in respect that although I have difficulty pricing "unlimited concrete" the myriad trucks and equipment involved threaten the cost of a concrete pyramid any ways. The only way to further justify such an endeavour is a. Expand the foundation into a plaza of swimming pools or b start a cement company
>>2260804For furthermore is it my pleasure I add
HOLY SHIT you schizo fuck GET OFF MY THREAD! I READ ALL YOUR RANTING GARBAGE AND NOW I WANT TO KILL YOU
>>2260557Coat your ceramic wool in refractory cement, it won't tolerate forging temperatures on it's own and fibers can come loose and be blown out into the air (and thus your lungs) if it's not contained. Cut it with fabric shears, wear a dust mask and eyepro, package it up in a bag or something when you aren't actively going to be cutting it for something new, vacuum the work area you cut it on afterwards.
>>2219242yummy cancer taste
Can I build a wax burnout oven/kiln? Or should I just buy one for ~$700?
>>2250461How did you make a chain?
>>2261500Get a single-layer pottery kiln (the ones where you get get like 20 sections to make a tall one) and stack cheap firebricks as needed on the top. Melt-out and drying doesn't need a lot of heat just a lot of time.
I've got thousands of small tungsten carbide pieces I want to melt down into half inch by 4 inch bars any recs for something to use as a mold?